中性快速固化硅酮密封胶，适用于一般密封及粘结如门窗、金属屋顶、排水沟、对玻璃、铝、不锈钢、砖、陶瓷及大部分金属及塑料均有极强粘结力。
主要性能特点:
1.单组分，易于操作
2.中性固化，无强烈的气味
3.快速固化
4.维持很好的柔韧性
5.与玻璃，大部分金属和塑料有极强粘结力
6.七种颜色可供选择：透明，白色，灰色，浅灰色，黑色，银色，棕色
包装：300ml硬支装，24支一箱

未固化的特性      
外观                                  膏状
邵氏硬度°A                     18                  ASTM C661
下垂度（W=20mm）         0                  JIS A1439
操作时间                        10分钟   
不粘手时间                     20分钟                JIS A1439
固化时间                         2天           8mm深**23℃，55%相对温度
已固化的特性   
外观                              弹性橡胶状      
挤用性                          ＞300ml/min     
抗拉强度              ＞1.2Mpa               ASTM D412
拉伸率                  350%                 ASTM D412
固化后使用温度        -53~149℃              ADCT-13A
弹性回复率                   ＞90%      
接口位移承受能力       ±25%                ASTM C719 
很适合用于出口，主要是因为污染指标测试

Brand: GE
Model: 168 neutral silicone sealant
  
Basic parameters
Uses: water, cracking, weathering
Size: 300ml hard sticks, a box of 24
Storage period: 12 months
 
Technical parameters
Elongation: 350%
Surface drying time (hours): 20 minutes
Melting point: 149 ℃
Freezing Point: -53 ℃
Tensile strength: 1.2 mPa
Neutral fast curing silicone sealant for general sealing and bonding, such as ** and doors, metal roof, gutters, glass, aluminum, stainless steel, bricks, ceramics and most metals and plastics are extremely strong bond strength.
Main features:
1. One-part, easy to operate
2. Neutral cure, no strong odor
3. Fast curing
4. To maintain good fle**bility
5. And glass, most metals and plastics h**e strong adhesive force
6. Seven colors: transparent, white, gray, light gray, black, si**er, brown
Packaging: 300ml hard sticks, a box of 24

Uncured properties
Appearance paste
Hardness ° A 18 ASTM C661
Ptosis degree (W = 20mm) 0 JIS A1439
Operating time 10 minutes
Sticky time of 20 minutes JIS A1439
Curing time of 2 days 8mm deep ** 23 ℃, 55% relative humidity
Characteristics h**e been cured
Elastic rubber-like appearance
Crowded with sexual> 300ml/min
The ma**mum tensile strength> 1.2Mpa ASTM D412
The ma**mum tensile rate of 350% ASTM D412
After curing temperature -53 ~ 149 ℃ ADCT-13A
Elastic recovery rate of> 90%
Interface displacement capacity of ± 25% ASTM C719
Very suitable for export, mainly because of pollution indi**or test